7/28/2019 Clasele de Otel 10025
1/2
DESTINATIILE UZUALE ALE CLASELOR DE OTEL PROFILAT CONFORMEN 10027 : 1992, EN 10025 : 1993 si 10113 : 1993
Exemplu: S355J2G3Z35
S Grupa de otel (S - otel profilat)
355 XXX - Elasticitatea minima (N/mm)
J2 Rezistenta la incovoiere
min. 27 J JR JO J2 J3 J4
min. 40 J KR KO K2 K3 K4Temp. C 20 0 -20 -30 -40
G3 Caracteristici fizice
Grupa 1 M - Laminare termomecanica
N - Laminare normalizata
G1 - Necalmat
G2 - Calmat
G3 - Conditie optionala de livrare
G4 - Conditie de livrare
Grupa 2 L - Pentru temperaturi scazute
M - Laminare termodinamica
N - Laminare normalizata
O - Offshore
W - Dezagregare
Z35 Cerinte speciale
Z15 - comprimare min. 15%
Z25 - comprimare min. 25%
Z35 - comprimare min. 35%
PROPRIETATILE MECANICE ALE CLASELOR DE OTEL PROFILAT
Standard ClasaElasticitate minima
N/mm2
Rezistenta larupere
la tractiune (Rm)N/mm2
Alungire minima%
Incercarea dinamicade reziliere
Grosime nominala
(mm)Grosime nominala
(mm)Grosime nominala
(mm)Temperatura
Energiaminima
absorbita
16>1640
>4063
>6380
>80100
>100150
3100
>100150
340
>4063
>63100
>100150
C J
EN 10025 : 1993S 235 JRG2
S 235 JO235 225 215 195 340 - 370 26 25 24 22
+200
2727
S 275 JRS 275 JO
275 265 255 245 235 225 410 - 560 400 - 540 22 21 20 18+20
02727
S 355 JRS 355 JO
S 355J2G3/G4
S 355K2G3/G4
355 345 335 325 315 295 490 - 630 470 - 630 22 21 20 18+20
0
2727
2740
EN 10113-3 :1993
S 355 MS 355 ML
355 345 335 450 - 610 22-20-50
4027
S 420 M
S 420 ML
420 400 390 500 - 660 19-20
-50
40
27
S 460 M
S 460 ML460 440 430 530 - 720 17
-20-50
4027
-
7/28/2019 Clasele de Otel 10025
2/2
COMPOZITIA CHIMICA A ANALIZEI OALEI DE TURNARE
Standard Clase Cmax %
Grosime nominala(mm)
Mnmax%
Simax%
Pmax%
Smax%
Nmax %
Al(1)max%
Nbmax%
Vmax%
CEV(7)max %
Grosime nominala (mm)
100>16100
16100
63
150
EN 10025 :1993 (6)
S 235 JRG2S 235 JO
0.170.17
0.170.17
0.200.17
1.41.4
--
0.0450.040
0.0450.040
0.009 (4)(5)
0.009 (4)(5)
0.350.35
0.350.35
0.380.38
0.380.38
S 275 JRS 275 JO
0.210.18
0.210.18
0.220.18
1.51.5
--
0.0450.040
0.0450.040
0.009 (4)(5)
0.009 (4)(5)
0.40 0.40 0.42 0.42
S 355 JRS 355 JO
S 355J2G3/G4
S 355K2G3/G4
0.240.200.20
0.20
0.240.20 (3)0.20 (3)
0.20 (3)
0.240.220.22
0.22
1.61.61.6
1.6
0.550.550.55
0.55
0.0450.0400.035
0.035
0.0450.0400.035
0.035
0.009 (4)(5)
0.009 (4)(5)
--
0.450.450.45
0.45
0.450.450.45
0.45
0.470.470.47
0.47
0.470.470.47
0.47
EN 10113-3 :1993 (2)
S 355 MS 355 ML
0.160.16
0.160.16
0.160.16
1.61.6
0.500.50
0.0350.030
0.0300.025
0.0150.015
0.020.02
0.050.05
0.100.10
0.390.39
0.390.39
0.400.40
0.450.45
S 420 M
S 420 ML0.180.18
0.180.18
0.180.18
1.71.7
0.500.50
0.0350.030
0.0300.025
0.0200.020
0.020.02
0.050.05
0.120.12
0.430.43
0.450.45
--
--
S 460 M
S 460 ML0.180.18
0.180.18
0.180.18
1.71.7
0.600.60
0.0350.030
0.0300.025
0.0250.025
0.020.02
0.050.05
0.120.12
0.450.45
0.460.46
--
--
* OBSERVATII:(1) Daca exista suficiente elemente care fixeaza azotul conditia de Al minim nu se aplica(2) Suma totala a Cr, Cu and Mo nu trebuie sa fie mai mare de 0.60%.(3) Pentru grosime nominala >30mm: C=0.22% max(4) Este admisa depasirea valorilor specificate cu conditia ca pentru fiecare majorare de 0.001% N continutul maxim de P va fi redus cu0.005%; continutul N a oalei de turnare nu poate fi mai mare de0.012%.(5) Valoarea maxima de nitrogen nu se aplica daca compozitia chimica prezinta o compozitie minima de Al de 0.020% sau daca suntprezente suficiente elemente care fixeaza N. Elementele care fixeaza N vor fi mentionate in controlul documentului.(6) Grosimea nominala >100mm: Continutul C dupa acord.(7) CEV = C + Mn/6 + (Cr+Mo+V)/5 + (Cu+Ni)/15 = cerinta suplimentara.