GHIDPRIVIND CORESPONDENTA MATERIALELOR

(valabil pentru mentenanta mijloacelor)F115.20-04-002RA, vers 01

UZ INTERN : AUTOMOBILE DACIA

Data elaborarii: martie 2004

Elaborat : Vasile BAIASU

CUPRINS 1. OTELURI LAMINATE SI TRASE

1.1. OTEL DE UZ GENERAL PENTRU CONSTRUCTII

1.2. OTEL CARBON DE CALITATE PENTRU TRATAMENT TERMIC, DESTINAT CONSTRUCTIEI DE MASINI

1.3. OTEL PENTRU ARCURI

1.4. OTEL ALIAT PENTRU TRATAMENT TERMIC IN CONSTRUCTIA DE MASINI

1.5. OTEL RAPID PENTRU SCULE

1.6. OTEL PENTRU SCULE

1.7. OTEL ALIAT PENTRU SCULE

1.8. OTEL REZISTENT LA COROZIUNE SI 14414p1519o REFRACTAR, PRELUCRAT LA CALD

1.9. OTEL INOXIDABIL SI REFRACTAR

1.10. OTEL PENTRU RULMENTI

1.11. OTEL REZISTENT LA UZURA

1.12. OTEL PENTRU AUTOTURISME DACIA

1.13. OTEL PENTRU TABLE DESTINATE CAZANELOR SI RECIPIENTELOR SUB PRESIUNE, PENTRU TEMPERATURA AMBIANTA RIDICATA

1.14. OTEL PENTRU TABLE DESTINATE CAZANELOR SI RECIPIENTELOR SUB PRESIUNE, PENTRU TEMPERATURA AMBIANTA SI SCAZUTA

1.15. OTEL PENTRU AUTOTURISME DACIA

1.16. OTEL PENTRU TEVI UTILIZATE LA TEMPERATURI RIDICATE

1.17. OTEL CU GRANULATIE FINA PENTRU TABLE DESTINATE CONSTRUCTIILOR SUDATE

1.18. OTEL PENTRU TEVI UTILIZATE LA TEMPERATURI SCAZUTE

1.19. OTEL PENTRU TABLE SI BENZI DESTINATE AMBUTISARII

1.20. OTEL PENTRU TABLE SI BENZI LAMINATE LA RECE DESTINATE CAROSERIILOR AUTO

1.21. OTEL REZISTENT LA COROZIUNE

1.22. OTEL PENTRU AUTOMATE

1.23. OTEL PENTRU PINIOANE

1.24. OTEL PENTRU ORGANE DE ASAMBLARE

1.25. OTEL PENTRU TEVI FARA SUDURA, DE UZ GENERAL

1.26. OTEL PENTRU SUPAPELE MOTOARELOR CU ARDERE INTERNA

1.27. OTEL PENTRU SUPAPE EVACUARE

1.28. OTEL TERMOREZISTENT PENTRU ORGANE DE SAMBLARE

2. OTELURI TURNATE

2.1. OTEL SLAB ALIAT SI ALIAT TURNAT IN PIESE

2.2. OTEL AUSTENITIC MANGANOS TURNAT IN PIESE

2.3. OTEL TURNAT IN PIESE PENTRU ARMATURI

2.4. OTEL CARBON, SLAB ALIAT REZISTENT LA TEMPERATURI RIDICATE, TURNAT IN PIESE

3. FONTE

3.1. FONTE CU GRAFIT LAMELAR

3.2. FONTE CU GRAFIT NODULAR

3.3. FONTE MALEABILE

3.4. FONTE CU GRAFIT NODULAR CU STRUCTURA BAINITICA

1. OTELURI

Recomandari de utilizare:

Corespondenta marcilor de oteluri laminate sau trase este in conformitate cu STAS R 4400/1-80.

Corespondenta indicata este aproximativa si data cu titlu informativ. Ea este stabilita pe baza : compozitiei chimice, caracteristicilor mecanice si a conditiilor de utilizare.

Pentru marcile straine indicate intre paranteze corespondenta stabilita este foarte larga.

1.1. OTEL DE UZ GENERAL PENTRU CONSTRUCTII

STAS 500/2-80 NFA 35-501-77

DIN 17100Marca Numar

OL 34.1 A 34-1 USt 34-1 1.0055OL 37.1

OL 37.2

OL 37.2k

OL 37.3

OL 37.4

E 24-1

E 24-2 (S235JR)

E 24-2NE

E 24-3

E 24-4

USt 37-1

USt 37-2

RSt 37-2

St 37-3

St 37-3

1.0065

1.0036

1.0038

1.0116

1.0116OL 42.1

OL 42.1k

OL 42.2

OL 42.2k

OL 42.3

-

E 26-1

E 26-1NE

E 26-2

E 26-2NE

E 26-3

E 26-4

USt 42-1

RSt 42-1

USt 42-2

RSt 42-2

St 42-3

St 42-3

1.0075

1.0077

1.0040

1.0042

1.0136

1.0136OL 44.2(k)

OL 44.3(k)

OL 44.4(k)

E 30-2

E 30-3

E 30-4

RSt 46-2

St 46-3

St 46-3

1.0477

1.0483

1.0483OL 52.2(k)

OL 52.3(k)

OL 52.4(k)

E 36-2

E 36-3

E 36-4

-

St 52-3

St 52-3

-

1.0570

1.0570OL 50(k) A 50-2 St 50-2 1.0050OL 60(k) A 60-2 St 60-2 1.0060OL 70(k) A 70-2 St 70-2 1.0070OL 30 A 33-1

A 33-2

St 33-1

St 33-2

1.0033

1.0035

1.2. OTEL CARBON DE CALITATE PENTRU TRATAMENT TERMIC, DESTINAT CONSTRUCTIEI DE MASINI

STAS 880-80 NF

A 35-551-72

A 35-552-72

DIN

17200-69

17210-69Marca Numar

OLC 10OLC 10 X

CC 10 , (AF 34 C 10)*XC 10

C 10Ck 10

1.0301

1.1121OLC 15

OLC 15 X

AF 37 C 12)*

XC 18, (XC 15)

C 15

Ck 15

1.0401

1.1141OLC 20 CC 20 - -OLC 25

OLC 25 X

(AF 42 C 20)*

XC 25, (XC 18)

C22

Ck 22

1.0402

1.1151OLC 35

OLC 35 X

CC 35, (AF 55 C 35)*

XC 38, (XC 35), (XC 32)

C 35

Ck 35

1.0501

1.1181OLC 45

OLC 45 X

CC 45,(AF 65 C 45)*

XC 48, (XC 45), (XC 42)

C 45

Ck 45

1.0503

1.1191OLC 55

OLC 55 X

XC 55, (XC 54) C 55

Ck 55

1.0535

1.1203OLC 60

OLC 60X

(AF 70 C 55)*

XC 60, (XC 65)

C 60

Ck 60

1.0601

1.1221

*simbolizare veche

1.3. OTEL PENTRU ARCURI

STAS 795-80 NF

A 35-551-72

A 35-552-72

A 35-571-74

DIN

17221-72

17222-72Marca Numar

OLC 55 A XC 55 Ck 55 1.1203OLC 65 A

(OLC 66 S

STAS 8371-80)

XC 68 (XC 65) Ck 67 1.1231

OLC 75 A XC 75 Ck 75 1.1248OLC 85 A - Ck 85 1.1269

51 Si 17 A 51 S 7 51 Si 7 1.090340 Si 17 A (45 S 7) - -51 VCr 11 A 50 CV 4 50CrV 4 1.815956 Si 17 A 55 S 7 55 Si 7 1.090460 Si 15 A - 60SiCr7 1.710865 S 2 WA

(STAS 11514-80)

- - -

1.4. OTEL ALIAT PENTRU TRATAMENT TERMIC IN CONSTRUCTIA DE MASINI

STAS 791-80 NF

A 35-551-72

A 35-552-72

A 35-571-74

DIN

17210-69

17200-69Marca Numar

15 Cr 08 - (15 Cr 3) 1.701518 MnCr 10 16 MC 5 16 MnCr 5 1.713121 MoMnCr 12 (18 CD 4) - -18 MoCrNi 13 18 NCD 6

18 CND 617 CrNiMo 6 1.6587

13 CrNi 30 (14 NC 11)

(16 NC 11)

(14 NiCr 10) 1.5732

20 MoNi 35 - - -21 TiMnCr 12 - - -28 TiMnCr 12 - - -35 Mn 16 - - -65 Mn 10 - 65 Mn 4 1.281735 MnSi 12 - 37 MnSi 5 1.512240 Cr 10 42 C 4 41 Cr 4 1.703540 BCr 10 - - -33 MoCr 11 34 CD 4

(35 CD 4)

34 CrMo 4 1.7220

41 MoCr 11 (38 CD 4)

40 CD 4

42 CD 4

42 CrMo 4 1.7225

50 VCr 11 50 CV 4 50 CrV 4 1.815934 MoCrNi 15 (35 NCD 6) 34 CrNiMo 8 1.658230 MoCrNi 20 30 CND 8 30 CrNiMo 8 1.6580

30 NCD 838 MoCrAl 09 (40 CAD 6.12) (34 CrAlMo 5)

(41 CrAlMo 7)

1.8507

1.850941 CrNi 12 (30 NC 12) (31 NiCr 14) 1.575218 CrNi 20 20 NC 6 18 CrNi 8 1.5920

1.5. OTEL RAPID DE SCULE

STAS 7382-80 NFA 35-590-78

SEW

320-69Marca Numar

Rp 1 - - -Rp 2 Z 80 WKCV 18.05.04.01 HS 18-1-2-5 1.3255Rp 3 (Z80 WCV 18.04.01) HS 18-0-1 1.3355Rp 5 Z 85 WDCV 06.05.04.02 HS 6-5-2C 1.3343Rp 9 - HS 3-3-2 1.3333Rp 10 Z 85 DCWV 08.04.02.02 HS 2-9-1 1.3346- Z 110 WKDV 07.05.04.02 HS 7-4-2-5- Z 120 WDV 06 HS 6-5-3- Z 150 WKV 12 HS 12-4-5-5- Z 110 DKWV 09.08.02.01 HS 2-9-1-8- Z 160 WDV 06 HS 6-5-3- Z 110 DK 09 (lame de forma,

scule GLEASON)

1.6. OTEL PENTRU SCULE

STAS 1700-80 NF

A 35-590-78

SEW

150-71Marca Numar

OSC 7 Y1 70 (C 67 W3) 1.1744OSC 8 Y1 80

Y1 90

C 80 W 1

C 80 W 2

1.1525

1.1625OSC 10 Y1 105 (C 105 W 1)

(C 105 W 2)

1.1545

1.1645OSC 11 - C 110 W 2 1.1654OSC 13 - (C 125 W 1) 1.1560

-

-

(C 125 W 2)

(C 135 W 2)

1.1663

1.1673

1.7. OTEL ALIAT PENTRU SCULE

STAS 3611-80 NF

A 35-590-78

SEW 200-69

SEW 250-70Marca Numar

MCV 14 105 WC 13 105 WCr 6 1.2419VM 18 90 MV 8 90 MnCrV 8 1.2842CW 20 (105 WC 13) (105 WCr 6) 1.2419C 120 Z 200 C 12 X 210 Cr 12 1.2080VMoC 120 Z 160 CDV 12 X 153 CrMoV 12 1.2601CV 06 - 115 CrV 3 1.2210VCW 85 Z 30 WCV 9 X 30 WCrV9 3 1.2581MoCN 15 - 55 NiCrMoV 6 1.2713VMoCN 17 55 NCDV 7 56 NiCrMoV 7 1.2714MoVC 30 32 DCV 5 X 32 CrMoV 3 3 1.2365- 35 CDV 5 X 100 CrMoV 5MoVC 50.10 Z 38 CDV 5 X 37 CrMoV 5 1 1.2343MoVC 50.13 Z 40 CDV 5 X 40 Cr MoV 5 1 1.2344MoWC 53 - X 37 CrMoW 5 1 1.2606VSCW 20 - 45 WCrV 7 1.2542

1.8. OTEL REZISTENT LA COROZIUNE SI REFRACTAR, PRELUCRAT LA CALD

STAS 3583-80 NF

A 35-572-75

A 35-578-70

DIN 17440-72


12 Cr 130 Z 12 C 13 X 10 Cr 13 1.400620 Cr 130 Z 20 C 13 X 20 Cr 13 1.402130 Cr 130 Z 30 C 13 X 30 Cr 13 1.402840 Cr 130 - X 40 Cr 13 1.40348 (Ti)Cr 170 Z 8 C 17 X 8 Cr 17

X 6 Cr Ti 17

1.4016

1.451012 NiCr 180 (Z 10 CN 18.09) X 12 CrNi 18 8 1.430010 TiNiCr 180

(STAS 10322-80)

Z 6 CNT 18.10 X 10 CrNiTi 18 9 1.4541

10 TiMoNiCr 175 Z 6 CNDT 17.12 X 10 CrNiMoTi 18 10 1.457115 SiNiCr 250

(Cr 25 Ni 20

STAS 11510-80)

Z 12 CNS 25.20 X 15 CrNiSi 25 20 1.4841

1.9. OTEL INOXIDABIL SI REFRACTAR

STAS 11523-80 NF

A 35-572-75

A 35-576-75

A 35-578-70

A 35-583-75

DIN 1770-72

SEW 400-73

SEW 470-76SEW 670-69

Marca Numar

7 AlCr 130 Z 6 CA 13 X 7 CrAl 13 1.400222 NiCr 170 Z 15 CN 16.02 X 22 CrNi 17 1.405790 VmoCr 180 Z 100 CD 17 X 90 CrMoV 18 1.411235 MoCr 165 - X 35 CrMo 17 1.41222 NiCr 185 Z 2 CN 18.09

Z 2 CN 18.10

X 2 CrNi 18 9 1.4306

2 MoNiCr 175 Z 2 CND 17.12 X 2 CrNiMo 18 12 1.44352 CuMoCrNi 250 Z 1 NCDU 25.20 (X 2 NiCrMoCu 25 21) 1.453610 AlCr 240 Z 10 CAS 24 X 10 CrAl 24 1.476215 SiNiCr 200 Z 15 CNS 20.15 X 15 CrNiSi 20 12 1.482812 NiCr 250 Z 12 CN 25.20 X 12 CrNi 25 21 1.48452 NiCr 250 Z 2 CNNb 25.20 (X 5 CrNi 25 21) 1.433512 SiCrNi 360 Z 12 NCS 35.16 X 12 NiCrSi 36 16 1.486440 SiCrNi 380 - X 40 NiCrSi 36 16 1.486510 TiAlCrNi 320 - X 10 NiCrAlTi 32 20 1.487612 TiNiCr 180 Z 6 CNT 18.12 B X 12 CrNiTi 18 9 1.487819 MoCr 120 - X 19 CrNiTi 12 1 1.492120 VWMoCr 120 - X 20 CrMoWV 12 1 1.4935(5 NiCr 180) Z 6 CN 18.09

Z 6 CN 18.10

X 5 CrNi 18 9

X 5 CrNi 18 10

1.4301

1.10. OTEL PENTRU RULMENTI

STAS 1456/1-80 NFA 35-565-70


RUL 1 100 C 6 100 Cr 6 1.3505

RUL 2 - 100 CrMn 6 1.3520

1.11. OTEL REZISTENT LA UZURA

STAS 11513-80 NF

A 35-551-72

A 35-552-72

DIN

17200-69

17115-72Marca Numar

20 Mn 10 (20 M 5) 28 Mn 6 1.117040 Mn 10 (35 M 5) 40 Mn 4 1.1157

1.12. OTEL PENTRU TABLE GROASE DESTINATE RECIPIENTILOR SUB PRESIUNE, CU CONDITII SPECIALE DE CALITATE

STAS 11502-80 NF

A 35-501-77

A 35-201-75


RV 52 E 355 TTStE 36 1.0566R 55 E 420 TTStE 43 1.8912R 58 E 460 TTStE 47 1.891509 Mn 16 E 30-3

E 30-4

- -

1.13. OTEL PENTRU TABLE DESTINATE CAZANELOR SI RECIPIENTELOR SUB PRESIUNE, PENTRU TEMPERATURA AMBIANTA RIDICATA

STAS 2883/3-80 NF

A 36-205-79

A 36-206-78

DIN 17155-59Marca Numar

K 41 A 42 CP H II 1.0425K 47 A 48 CP 17 Mn 4 1.0481K 52 A 52 CP 19 Mn 5 1.048216 Mo 3 15 D 3 15 Mo 3 1.541514 CrMo 4 15 CD 4.05 13 CrMo 4 4 1.7335

1.14. OTEL PENTRU TABLE DESTINATE CAZANELOR SI RECIPIENTELOR SUB PRESIUNE, PENTRU TEMPERATURA AMBIANTA SCAZUTA

STAS 2883/2-80 NF

A 36-205-79

A 36-208-79

DIN 17135-64

SEW 089-70; SEW 680-70Marca Numar

R 37 A 37 AP ASt 35

TTSt 35

1.0346

1.0356R 44 A 48 AP

A 48 FP

(05 N 285)

ASt 45

TTSt 41

TTStE 29

1.0436

1.0437

1.0488R 52 A 52 AP

A 52 FP

(05 N 355)

ASt 52

TTStE 36

1.0577

1.0566

1.15. OTELURI PENTRU AUTOTURISMELE DACIA 1300

STAS 11500/2-80 NF

A 35-551-72

A 35-552-72

A 35-571-74

DIN

17200-69

17210-69

17221-72Marca Numar

38 Cr 05 38 C 2 38 Cr 2 1.7003OLC 42 XC 42 - -32 Cr 10 32 C 4 32 Cr 4 1.703337 Cr 10 38 C 4 37 Cr 4 1.703412 MoCr 10 - (13 CrMo 4) 1.733516 MoCr 10 16 CD 4

(18 CD 4)

- -

20 MoCr 10 20 CD 4 - -30 MoCr 10 30 CD 4 - -33 MoCr 10 34 CD 4

(35 CD 4)

34 MoCr 4 1.7220

20 NiCr 15 20 NC 6 (18 CrNi 8) 1.592035 MoCrNi 40 35 NCD 16 - -16 CrMn 12 16 MC 5 16 MnCr 5 1.7131

X 61 SC 7 60 SiCr 7 1.0961

1.16. OTEL PENTU TEVI UTILIZATE LA TEMPERATURI RIDICATE

STAS 8184-80 NF

A 49-811-73

A 36-206-78

DIN

17115-59Marca Numar

OLT 35 K TU 37- C St 35.8 1.0305OLT 45 K TU 48-C St 45.8 1.040516 Mo 3 15 D 3 15 Mo 3 1.541514 CrMo 4 15 CD 4.05 13 CrMo 4 4 1.733510 CrMo 10 10 CD 9.10 10 CrMo 9 10 1.7380

16 MoCr 50 - 12 CrMo 19 5 1.7362

1.17. OTEL CU GRANULATIE FINA PENTRU TABLE DESTINATE CONSTRUCTIILOR SUDATE

STAS 9021-80 NF

A 36-201-75


OCS 44 - TTStE 29 1.0488OCS 52 E 355 TTStE 36 1.0566OCS 55 E 420 TTStE 43

WstE 43

1.8932

1.8912OCS 58 E 460 TTSt E 47

WstE 47

1.8915

1.8935

1.18. OTEL PENTRU TEVI UTILIZATE LA TEMPERATURI SCAZUTE

STAS 10382-80 NF

A 36-208-79


OLT 35 R - TTSt 35 1.0356OLT 45 R - - -10 Ni 35 (3,5 N 355) 10 Ni 14 1.5637

1.19. OTEL PENTRU TABLE SI BENZI DESTINATE AMBUTISARII

STAS 9485-80 NF DIN 1623-72

A 36-401-69

A 35-301-71

Marca Numar

A 1 TC St 12 1.0330A 2 E St 13 1.0333A 3 (ES) St 14 1.0338A 3 Ck

(STAS 11509-80)

3 C St W 24 1.0335

1.20. OTEL PENTRU TABLE SI BENZI LAMINATE LA RECE, DESTINATE CAROSERIILOR AUTO

STAS 10318-80 NF

A 36-401-69


A 4 E (St 13) 1.0333A 5 ES (St 14) 1.0338

1.21. OTELURI REZISTENTE LA COROZIUNE

STAS 500/3-80 NF

A 35-502-79RCA 37 (E 24 W)RCA 52 (E 36 WB)

1.22. OTEL PENTRU AUTOMATE

STAS 1350-80 NF

A 35-562-78


AUT 12 (10 F 1) (10 S 2) 1.0721AUT 20 - (22 S 20) 1.0724AUT 30 - (35 S 20) 1.0726AUT 40 M (45 MF 6) (45 S 20) 1.0727

1.23. OTEL PENTRU PINIOANE

STAS 11512-80 NF

A 35-551-72

A 35-552-72


17 CrNiMo 6 18 NCD 6 17 CrNiMo 6 1.6587

1.24. OTEL PENTRU ORGANE DE ASAMBLARE

STAS 11511-80 NF

A 35-551-72

A 35-552-72

DIN (norma tehnica interna)Marca Numar

20 MnB 5 20 MB 5 20 MnB 3 1.5507

1.25. OTEL PENTRU TEVI FARA SUDURA, DE UZ GENERAL

STAS 8183-80 NF DIN 1629-61Marca Numar

OLT 35 St 35 1.0308OLT 45 St 45 1.0408OLT 65 - -

1.26. OTEL PENTRU SUPAPELE MOTOARELOR CU ARDERE INTERNA

STAS 11311-80 NF

A 35-579-70

DIN (dupa norma interna)Marca Numar

45 SiCr 85 Z 45 CS 9 (X 45 CrSi 9 3) 1.4718

1.27. OTEL PENTRU SUPAPE DE EVACUARE

STAS 11524-80 NF

A 35-579-70

DIN (dupa norma interna)Marca Numar

45 SiCr 95 45 CS 9 X 45 CrSi 9 3 1.471880 SiNiCr 200 Z 80 CSN 20.02 X 80 CrNiSi 20 1.474753 NNiMnCr 210 Z 52 CMN 21.09 X 53 CrMnNiN 21 9 1.4871

1.28. OTEL TERMOREZISTENT PENTRU ORGANE DE ASAMBLARE

STAS 11512-80 NF

A 35-558-69


24 VMoCr 12 28 CDV 5.08 24 CrMoV 5 5 1.773312 MoCr 90 - X 12 CrMo 9 1 1.7386

2. OTELURI TURNATE

Recomandari de utilizare :

Corespondenta marcilor de oteluri turnate este orientativa si in conformitate cu STAS R 4400/2-88,

Corespondenta indicata este aproximativa si data cu titlu informativ. Ea este stabilita pe baza : compozitiei chimice, caracteristicilor mecanice si a conditiilor de utilizare.

2.1. OTEL SLAB ALIAT SI ALIAT TURNAT IN PIESE

STAS 1773-82 NF

A 32-054-78

A 32-055-76

TGL

14395-85

T 20 Mn 14 20 M 6-M GS-20 Mn 6T 35 Mn 14 30 M 6-M GS-35 Mn 6T 40 Mn 11 - GS-45 Mn 4T 30 SiMn 12 FC-M -T 34 MoCr 09 25 CD 4-M GS-30 CrMo 4T 35 MoCrNi 08 - -T 26 VSiMn 14 30 MV6-M -T 20 TiMn 12 - -T 35 SiCrMn 11 - GS-40 MnCrSi 3T 30 MoCrNi 14 30 NCD 8-M GS-30 CrNiMo 6 T 14 VMoCuNi 16 - -T 40 VMn 17 - -poansoane, lame ascutite : 50 CD 4-Mpiese foarte solicitate la frecare : 32 NCD 14- M

matrite forja, scule de taiere si calibrare :

35 CDV 5-M

piese foarte solicitate cu duritate foarte ridicata :

Z160CDV 12- M

2.2. OTEL AUSTENITIC MANGANOS TURNAT IN PIESE

STAS 3718-87 NFA 32-058-84


T 105 Mn 120 -T 130 Mn 135 Z 120 M 12-M G-X 120 Mn 12T 120 CrMn 130 Z 120 MC 12-MT 100 NiMn 130 Z 100 MN 13.4-MT 100 MoMn 130 Z 110 MD 12.1-MT 35 NiCr 260 (Z 40 CN 25.20-M) G-X 40 CrNiSi 25 12 1.4837T 25 NiCr 250 G-X 15 CrNi 25 20 1.4840T 35 CrNi 370 G-X 40 CrNiSi 36 18 1.4865T 12 MoNiCr 210 - -

2.3. OTELURI TURNATE IN PIESE PENTRU ARMATURI

STAS 9277-84 NF

A 32-055-76

A 32-056-84


OTA 20 A 42 C-M GS-C 25 1.0619OTA 40Mn13 - - -OTA 30VMn13 - - -OTA 17MoCr13 15 CD 5.05-M GS-18CrMo9 10 1.7379OTA 23VWMoCr120 - G-X22CrMoV12 1 1.4931OTA 10NbMoNiCr170 Z 4 CNDNb 18.12-M G-X5CrNiMoNb18.10 1.4581OTA 10TiMoNiCr170 - - -

2.4. OTEL CARBON, SLAB ALIAT SI MEDIU ALIAT REZISTENT LA TEMPERATURI RIDICATE, TURNAT IN PIESE

STAS 12404-85 NF

A 32-055-85


T 21 A 42 C-M GS-C 25 1.0619T 16 Mo 5 - GS-22 Mo 4 1.5419T 16 MoCr 11 15 CD 4.05-M GS-17 CrMo 5 5 1.7357T 14 MoVCr 6 - - -T 21 VMoCr 10 NCDV 4.10-M - -T 17 VMoCr 14 15 CDV 9.10-M GS-17 CrMoV 5 11 1.7706T 15 MoWVCr 12 - - -

Notatii utilizate:

STAS -standard de stat Romania

NF -norma Franta

DIN, SEW - norme Germania

Simbolizarea elementelor chimice utilizate :

Denumirea in

l. romana

Simbolul dupa STAS

Simbol dupa NF

Simbol dupa

DIN, SEWAluminiu Al A AlNichel Ni N NiMolibden Mo D MoCrom Cr C CrCupru Cu U CuStaniu Sn E SnSulf (fosfor) S F S

Mangan Mn M MnPlumb Pb Pb PbAzot (nitrogen) N Az NSiliciu Si S SiTitan Ti T TiTugsten W W WVanadiu V V VZinc Zn Z ZnZirconiu Zr ZR ZrBor B B BNiobiu Nb Nb NbCobalt Co K

3. FONTE

3.1. FONTE CU GRAFIT LAMELAR

SR ISO 185-94 Simbol vechi

STAS 568-82

NF DINMarca Rm

N/mm2

Marca Numar

100 100 Fc 100 Ft 10 D GG-10 0.6010150 150 Fc 150 Ft 15 D GG-15 0.6015200 200 Fc 200 Ft 20 D GG-20 0.6020250 250 Fc 250 Ft 25 D GG-25 0.6025300 300 Fc 300 Ft 30 D GG-30 0.6030350 350 Fc 350 Ft 35 D GG-35 0.6035- 400 Fc 400 Ft 40 D GG-40 0.6040

FGL 175HB*FGL 215HB*FGL 240HB*

*Fonte prevazute pe echipamente RENAULT (E01.41.050.N):

3.2. FONTE CU GRAFIT NODULAR (SFEROIDAL)

SR ISO 5922-95 Simbol vechi

STAS 6071-82

NF DIN

Marca Rm

N/mm2

A

%

Marca Numar

Ft GjS 900-2 900 2 - - - - 800-2 800 2 Fgn 800-3 FGS 800.2 GGG-80 0.7080 700-2 700 2 Fgn 700-2 FGS 700.2 GGG-70 0.7070

600-3 600 3 Fgn 600-2 FGS 600.3 GGG-60 0.7060- - FGS 600-3A*

500-7 500 7 Fgn 500-7 FGS 500.7 GGG-50 0.7050 450-10 450 10 Fgn 450-5 - (GGG-40.3) 0.7043 400-15 400 15 - (FGS 400.12) GGG-40 0.7040 400-18 350 18 - - - - - - FGS 400-18A* 350-22 350 22 - (FGS 370.17) GGG-35.3 0.7033

*Fonte prevazute pe echipamente RENAULT (E01.45.030.N) :

3.3. FONTE MALEABILE

SR ISO 5922-95 Simbol

vechi

569-79

NF DINMarca Rm

N/mm2

A

%

Tip Marca Numar

W 35-04 350 4 cu

inima

alba

Fma 350 (MB 35.7) GTW-35 0.8035W 38-12 380 12 - - GTW-S38 0.8038W 40-05 400 5 Fma 400 (MB 40.10) GTW-40 0.8040W 45-07 450 7 - - GTW-45 0.8045

B 30-06 300 6 cu

inima

neagra

Fmn 300 - - -B 32-12 320 12 Fmn 320 - - -B 35-10 350 10 Fmn 350 MN 35.10 GTS-35 0.8135

P 45-06 450 6 perlitica

Fmp 450 GTS-45 0.8145P 50-05 500 5 Fmp 500 - - -P 55-04 550 4 Fmp 550 GTS-55 0.8155P 60-03 600 3 Fmp 600 - - -P 65-02 650 2 Fmp 650 GTS-65 0.8165P 70-02 700 2 Fmp 700 MP 70.2 GTS-70 0.8170P 80-01 800 1 -

3.4. FONTE CU GRAFIT NODULAR CU STRUCTURA BAINITICA

SR ISO 13169-94 Simbol

STAS

vechi

Marca Rm

N/mm2

A

%

HB

FgnB 800 800 10 260-320 nu exista

FgnB 900 900 8 280-340FgnB 1000 1000 5 300-380FgnB 1100 1100 3 360-420FgnB 1200 1200 2 380-450FgnB 1400 1400 - 450-550